Kim, GuntaeCorre, G.Vohs, John MIrvine, J. T. S.Gorte, Raymond J2023-05-222023-05-222008-02-142008-02-14https://repository.upenn.edu/handle/20.500.14332/5751Ceramic anodes for solid oxide fuel cells SOFCs were prepared by aqueous impregnation of nitrate salts to produce composites with 45 wt % La0.8Sr0.2Cr0.5Mn0.5O3 (LCSM)in a 65% porous yttria-stabilized zirconia (YSZ) scaffold. Scanning electron micrographs indicate that the LSCM coats the YSZ pores following calcination at 1473 K. Composites produced in this manner exhibit conductivities at 1073 K of approximately 1 S/cm in air and 0.1 S/cm in humidified H2. A SOFC with a composite anode composed of 45 wt % LSCM, 0.5 wt % Pd, and 5 wt % ceria exhibited maximum power densities at 1073 K of 1.1 and 0.71 W cm−2 in humidified (3% H2O) H2 and methane, respectively.Working Paper